M. Braic, V. Braic, M. Balaceanu, C. N. Zoita, A. Kiss, A. Vladescu, A. Popescu, R. Ripeanu, Structure and properties of Zr/ZrCN coatings deposited by cathodic arc method, Mater. Chem. Phys. 126 (2011) 818-825.

 

Title: Structure and properties of Zr/ZrCN coatings deposited by cathodic arc method

Abstract: Zr/ZrCN multilayers, with bilayer periods ranging from 4.4 to 70 nm, were deposited on C45 and M2 steels and Si substrates by the cathodic arc technique, in a CH(4) + N(2) atmosphere. The elemental and phase composition, modulation periodicity, texture, surface morphology, residual stress, hardness, adhesion, friction and wear behavior were investigated as a function of bilayer period and C/N ratio using AES, RBS, XRR, XRD and AFM techniques, surface profilometry, Vickers microhardness and scratch adhesion measurements, and tribological tests. Two types of Zr/ZrCN multilayers, with high and low C/(C + N) ratios (0.7 and 0.2, respectively) in the ZrCN sub-layer composition, have been prepared. The investigations indicated that the microchemical. microstructural, mechanical and tribological characteristics of the multilayered coatings depended on C/N ratio and bilayer period. For the optimum structure parameters (bilayer periods in the range 6-13 nm), the tribological performance of the multilayers was found to be superior to that of the ZrCN monolayers

Key words: Zr/ZrCN multilayers; Cathodic arc deposition; Composition and structure; Mechanical characteristics

Saturday the 23rd. Copyright © INOE 2012
Implemented by networks